When it comes to aluminum plate manufacturers, many people must know and know that they produce aluminum plates, but many of them still don't know what problems aluminum plate manufacturers need to pay attention to during production. Today, I will introduce the precautions for you.
1、拉伸必定要在鋁合金型材冷卻到50度以下方可移到拉伸架上進(jìn)行拉伸作業(yè)，溫度過高即拉伸既會燙壞人體，燙壞毛條，更因為不能消除鋁合金型材內(nèi)應(yīng)力而在時效前后呈現(xiàn)曲折，扭擰，功能不良等廢品。
1. When stretching, the aluminum alloy profile must be cooled to below 50 degrees before it can be moved to the stretching frame for stretching operation. If the temperature is too high, stretching will not only burn the human body and the wool top, but also lead to twists, twists, poor functions and other wastes before and after aging because the internal stress of the aluminum alloy profile cannot be eliminated.
2、拉伸量的操控在1%擺布，而且要注意拉伸量過高會發(fā)生頭中尾尺度誤差，外表水紋狀麻花(魚鱗)痕，延伸率低，硬度偏高發(fā)脆(塑性低)。東莞機(jī)械零件加工過低的拉伸量會使型材抗壓強(qiáng)度及硬度偏低，乃至?xí)r效(淬火)也無法提高硬度，型材易弧形曲折(俗稱大刀彎)。
2. The stretching amount is controlled at 1%, and it should be noted that if the stretching amount is too high, the head, middle and tail scale errors will occur, the appearance of the water textured fried dough twist (fish scale) marks, the elongation rate is low, and the hardness is high and brittle (low plasticity). The processing of mechanical parts in Dongguan is too low in tension, which will cause the low compressive strength and hardness of the profile, and even aging (quenching) can not improve the hardness. The profile is easy to be curved (commonly known as big knife bend).
3、為操控拉伸變形量和非常好的操控整條型材的尺度變化，電腦鑼加工要選用適宜的專用夾墊和適宜的方式方法。非常是開口料，圓弧料，懸臂料，以及曲折形狀的型材更要留意拉伸夾墊的合理有用運(yùn)用。
3. In order to control the tensile deformation and the size change of the whole profile very well, the computer gong processing should select appropriate special clamping pads and appropriate methods. In particular, it is necessary to pay attention to the reasonable and useful use of stretching clamping pads for open materials, arc materials, cantilever materials and zigzag shaped profiles.
4、留意寬厚比高的、懸壁長的、弧度大的、壁厚巨細(xì)懸殊的、形狀奇怪等型材的小腳、薄齒、長腿、圓弧面、傾斜面、開口、視點(diǎn)等的受力狀況，避免型材部分或點(diǎn)狀尺度變形、扭擰、螺旋等缺點(diǎn)發(fā)生。
4. Pay attention to the stress conditions of the feet, thin teeth, long legs, circular surfaces, inclined surfaces, openings, viewpoints, etc. of the profiles with high width thickness ratio, long overhanging walls, large radians, large wall thickness differences, and strange shapes, to avoid the deformation, twist, spiral and other defects of the profiles or point size.

5、因毛條有阻熱發(fā)出效果，裝飾外表需求高的鋁板必定要多上下前后翻轉(zhuǎn)，機(jī)械零件加工以利散熱均勻，減少因散熱不均結(jié)晶度不一然后發(fā)生的橫向亮斑缺點(diǎn)，非常是大寬面，壁偏厚鋁板更要留意。
5. As the wool sliver has the effect of heat resistance, the aluminum plates with high demand for decorative surfaces must be turned back and forth more frequently. Mechanical parts are processed to facilitate uniform heat dissipation and reduce the transverse bright spot defects that occur after uneven heat dissipation and different crystallinity, especially the aluminum plates with large wide surfaces and thick walls.
6、在取料和移動及拉伸過程中不得彼此碰擦、拉扯、堆疊、擁堵、纏繞在一起，應(yīng)彼此間預(yù)留必定的間隔。對易曲折、出料長短的鋁合金型材要及時處置，必要時作好彼此間的維護(hù)處置。
6. In the process of reclaiming, moving and stretching, it is not allowed to rub, pull, stack, jam and wind together, and a certain interval shall be reserved between them. The aluminum alloy profiles that are prone to twists and turns and discharge length shall be disposed in a timely manner, and the maintenance and disposal of each other shall be carried out when necessary.
以上就是鋁板廠家在進(jìn)行加工時一定要注意的事項，而且工作人員們也一定要知道這些，因為這會對自己的工作方便很多！關(guān)注我們的網(wǎng)站http://m.baihuiplaza.com，了解更多鋁板生產(chǎn)加工的事項。
The above are the precautions that aluminum plate manufacturers must pay attention to when processing, and the staff must also know these, because it will be much more convenient for their own work! Follow our website http://m.baihuiplaza.com Learn more about aluminum plate production and processing.